Physical Property | Test Standard | Data | Unit |
Proportion | ASTM D792 | 0.868 | G/Cm3 |
Melt Index190°C 2.16Kg | ASTM D1238 | 0.50 | G/10Min |
Mooney ViscosityML1+4121°C | ASTM D1646 | 33 | MU |
Hardness | Test Standard | Data | Unit |
Shore Hardness A 1S Compression Molding | ASTM D2240 | 70 | |
Shore Hardness D1S Compression Molding | ASTM D2240 | 20 | |
Mechanical Properties | Test Standard | Data | Unit |
Tensile Modulus Compression Molding | ASTM D638 | 2.60 | MPa |
Tensile Strength Fracture 510Mm / Min Compression Molding | ASTM D638 | 9.50 | MPa |
Elongation at break 510mm / min compression molding | ASTM D638 | 810 | % |
Tear Strength Type C | ASTM D624 | 37.3 | KN/M |
Bending Modulus | ASTM D790 | 15.2 | MPa |
Bending Modulus | ASTM D790 | 14.4 | MPa |
Thermal Performance | Test Standard | Data | Unit |
Vicat Softening | ASTM D1525 | 46.0 | °C |
Melting TemperatureDSC 10°C/Min | Internal Test Method | 55.0 | °C |
Glass Transition Temperature | Internal Test Method | -52.0 | °C |
Crystallization TemperatureDSC | Internal Test Method | 42.0 | °C |